PMI Foam Core is a lightweight, closed-cell structural core material made from polymethacrylimide (PMI) foam. It is widely used in high-performance composite sandwich structures where low weight, high stiffness, thermal stability, and excellent mechanical strength are required. PMI Foam Core is particularly suitable for aerospace composites, wind energy, high-speed transportation, and advanced sporting equipment.
 
FEATURE
Ultra-Lightweight:
Significantly reduces the overall weight of composite structures while maintaining excellent structural performance.
High Strength-to-Weight Ratio:
Provides outstanding stiffness and compressive strength for high-performance sandwich structures.
Excellent Thermal Stability:
Maintains reliable mechanical properties at elevated temperatures and is suitable for demanding composite processing conditions.
High Fatigue Resistance:
Offers excellent durability and long-term performance under repeated loading, vibration, and cyclic stress.
Low Water Absorption:
Its closed-cell structure provides low moisture uptake and excellent dimensional stability in demanding environments.
 
APPLICATION
Aerospace Composites:
Used in aircraft interior panels, radomes, fairings, fuselage components, and other high-performance composite structures.
Wind Turbine Blades:
Applied as a structural core in lightweight wind turbine blade components requiring high stiffness and fatigue resistance.
High-Speed Transportation:
Used in high-speed trains, aerospace transportation systems, and lightweight vehicle structures.
Sports & Recreation:
Applied in racing equipment, high-performance bicycles, surfboards, and other lightweight composite sporting products.
Advanced Industrial Composites:
Used in high-performance sandwich panels, UAV structures, radomes, and other lightweight structural components.
 
SPECIFICATION

Model

Property

Applicaiton

VICELL-P

The highest mechanicalproperty core material;

appropriate for autoclavemolding.

UAV, turbine blades, train body, sports equipment,medical equipment, radar

VICELL-PH

High temperature, up to 180°C, maintains stable property.

Aerospace, military project, private planes, UAV

VICELL-PT

High wave-transmission, broad molding methods

Radome, medical bed board

VICELL-PY

Stealthy property

National defense
 
PROPERTY INDEX

Model

Density

Kg/m3

ISO 845

Compressive Strength

Mpa

ISO 844

Tensile Strength

Mpa

ASTM D638

Tensile Modulus

Mpa

ASTM D638

Shear Strength

Mpa

DIN 53294

Shear Modulus

Mpa

DIN 53294

Vicell-PH40

Average Value

40

0.9

1.6

60

0.7

20

Minimum Value

35-50

0.6

1.3

50

0.6

10

Vicell-PH60

Average Value

60

1.3

2.1

85

1.1

30

Minimum Value

51-70

1.2

2

70

1

25

Vicell-PH80

Average Value

80

1.9

3.2

120

1.35

45

Minimum Value

71-90

1.7

3

110

1.1

34

Vicell-PH100

Average Value

100

2.7

4.5

130

1.8

60

Minimum Value

91-115

2.4

4

120

1.6

50

Vicell-PH130

Average Value

130

3.8

6

160

2.5

85

Minimum Value

116-150

3.3

4.5

130

2.1

60

*Specific products could be made according to customers’requirements.